Compocasting (semisolid-semisolid, SS) and its two variations: SL (semisolid- liquid) and LL (liquid-liquid) process routes are used to make Al reinforced. SUMMARY: Al18B4O33 particle and whisker reinforced magnesium alloy ( AZ91D and. ZK60) composites were fabricated by the compocasting. Compo-casting is a type of stir casting method where the metal is heated to semi- solid state instead of liquid state.

Author: Doujora Mikakree
Country: Liberia
Language: English (Spanish)
Genre: Video
Published (Last): 27 September 2014
Pages: 312
PDF File Size: 8.53 Mb
ePub File Size: 19.16 Mb
ISBN: 803-1-60178-900-4
Downloads: 30971
Price: Free* [*Free Regsitration Required]
Uploader: Dakazahn

The analysis showed that the sliding speed has the greatest influence on specific wear rate Composite are obtained using the compocasting procedure. The analysis has shown the presence of MML, which means that there was transfer of material from steel disc to composite block.

Compocasting Research Papers –

Corrosion processes have occurred in the composite matrix. Ads help cover our server costs. Tribological behavior of aluminum hybrid composites studied by application of factorial techniques.

In the paper were shown the test results of tribological characteristics of hybrid composites with alloy base A reinforced by SiC and graphite.

Tribological test results showed that, for the investigated conditions, both composites had improved wear resistance and similar coefficient of friction with the reference material gray cast iron. Click here to sign up. The local progress of corrosion compocastiny depth of the composite matrix was noticed in micro-cracks. The effects of load, sliding speed, weight percentage of graphite reinforcement, and sliding distance on the wear rate are One of the possible solutions for overcoming of poor The mechanical properties of the composite are improved in relation to the base alloy.

By the experimental plan, test is conducted under three different values of sliding speed, three different values of normal load, different sliding distances, and also different lubricants.

Tribological compocastjng are realized Al2O3 particles as reinforcement were added into the semi-solid A alloy by infiltration and admixing. The testing included sliding speeds of 0. The composites were obtained by a modified compocasting procedure.

  ENTRIAMO IN AZIENDA 2 TOMO 1 PDF

The composites were produced by compo casting technique and then subjected to the thermal treatment T4 regime. Sliding distance of m was constant.

MMCs based on hypoeutectic Al-Si alloy: The tests were done for different normal load values, sliding speeds, sliding distance, with and without lubrication. Tribological properties in dry sliding conditions.

Application of the compocasting process led to a transformation of a dendritic to a nondendritic structure of the compocasing alloy. Enter the email address you signed up with and we’ll email you a reset link.

In this paper, the basic characteristics microstructure and proocess and tribological compocastjng of two A Al-Si alloy base MMCs, reinforced with Al2O3 particles were analysed and compared with gray cast iron as a standard material for cylinder blocks.

Corrosion did not affect SiC particles in the composites. Using of Al-alloys for producing of engine cylinders and blocks, instead of gray cast iron, results with weight savings and lower fuel consumption and therefore reduced pollution. The main parameter analyzed in the paper is coefficient of friction obtained in the conditions with and without lubrication.

Hybrid composite specimen is obtained by compocasting procedure. This article analyzes the influence of graphite reinforcement, load, sliding speed, and sliding distance on tribological behavior of A aluminum matrix composites reinforced with silicon carbide and graphite using the full-factorial Hybrid composites are obtained by compo casting procedure. It was found that corrosion resistance of the composites decreased with increase in content of SiC particles.

A side by side investigation of the microstructure and hardness of the composite and the base alloy cast into a steel mould was done.

In the first group are the results that This paper presents a short summary of the researches conducted in past few years concerning the MMCs with A Al-Si alloy matrix and different second phase.

A regression analysis and experiment corroboration was conducted in order to verify the results of the optimization. Specific wear rate prediction was done using artificial neural network ANN. Composite materials were produced by the compocasting process using mechanical mixing of the matrix, i. One of the possible solutions for overcoming of poor Al-alloys tribological properties is using of different types of metal matrix composites MMCs.

  KAALAM MT VASUDEVAN NAIR PDF

Remember me on this computer. A side by side investigation of the microstructure and hardness of the composite and the base alloy Log In Sign Up.

A aluminium alloy is used as a base matrix alloy, Tribological tests are realized on tribometer with block on disc compact pair in Tribological Center of Faculty of Engineering in Kragujevac.

Skip to main content.

There was a problem providing the content you requested

Tribological testing have been conducted on a block-on-disc tribometer with three varying loads 10, 20 and 30 N and three sliding speeds 0. Help Center Find new research papers in: The results are divided in two groups. These samples were additionally pressed in a special tooling by which tensile test samples were obtained. Microstructural examinations were performed after day exposure of thermally treated composites in the sodium-chloride solution.

Tribological tests were performed on a block-on-disc tribometer without lubrication. In the first group are the results that concern the influences of amount and size of reinforcement Al2O3and in the second group are the results that concern the influences of type of reinforcement Al2O3 and SiC and graphite. This article analyzes the influence of graphite reinforcement, load, sliding speed, and sliding distance on tribological behavior of A aluminum matrix composites reinforced with silicon carbide and graphite using the full-factorial design.

The goal of the paper was to optimize the influencing parameters in order to minimize specific wear rate using the Taguchi method.